PRODUCT NAME SLX53 High Chloride Polyethylene Paint

BRIEF With high chlorinated polyethylene, modifier, pigments and fillers made of paint

FEATURES 
Good adhesion and hardness
Good burning and mildew resistance due to high chloride
Good water, corrosion and permeation resistance
Excellent resistance to rust, abrasion and weather.
Fast drying, construction is convenient

RESISTANCE GUIDE 
HEAT RESISTANCE Excellent
WEATHERABILITY Excellent
SOLVENTS Resists splash and spillage of aliphatic solvents
ACIDS Suitable for splash and spillage to inorganic acids
ALKALIS Suitable for splash and spillage to most alkalis
SALTS Excellent resistance to most alkali salts
WATER Excellent resistance to immersion in fresh and salt water
ABRASION Good when fully cured.

USES:Suitable for the protection of steel structure

TYPICAL PROPERTIES AND APPLICATION DATA  
COLOR                         Topcoat, Color      Primer, Iron Red
DENSITY                        1.3g/ cm3    
SOLIDS BY VOLUME              38%       
SPREADING RATE                7.3 m2/kg     (40um DFT)
 DRYING TIME(23℃)              Touch ≤2 Hr    Handle ≤24 Hr   
OVERCOAT INTERVAL(23℃)      Min 8 Hr   Max  unlimited
 STORAGE (dry, cool )              At least 12 months
PACKAGING                     22kg per barrel 
FLASH POINT                     23℃

DIRECTIONS Stir contents of each can thoroughly with a broad flat stirrer using a stirring, lifting action or use a power mixer. Rate of cure will vary depending on temperature and other factors such as ventilation, film thickness, humidity, thinner. The temperature of stir will >15℃, otherwise thinner should be added for needed viscosity after stir.
Overmuch thinner will lead sag and slow cure rate, thin film. Practical spreading rates may be reduced 5-25% for wastage of different application conditions.

APPLICATION  STEEL: Round off all rough welds, sharp edges and remove weld spatter. Remove grease, oil and other contaminants. Steel surface must be prepared by abrasive blast cleaning to ISO Standard Class Sa2.5 or power tool cleaning Class St3.
Don’t apply at air temperature below 5℃ or above 40℃. Don’t apply at relative humidity above 85% or when air temperature is less than 3℃ above the dew point.
Don’t apply if there is fog, rain, snow or strong wind. 
BRUSH/ROLLER: Suitable for small areas only. Apply even coats of the mixed material to the prepared surface. Thin if necessary with up to 0-15% with High Chloride Polyethylene Thinner X-4. Additional coats may be required to attain specified thickness. 
CONVENTIONAL SPRAY: Thinning is not normally required, however 0-15% of High Chloride Polyethylene Thinner X-4 can be added.
AIRLESS SPRAY: Thinning is not normally required, however 0-15% of High Chloride Polyethylene Thinner X-4 can be added. Pump ratio is 23:1 or 32:1 and fluid tip is 0.38-0.43 mm.
Overcoating: Aged coating should be tested for lifting by a method such as ‘X’cut or crosshatch methods. If it lifts, remove it. The surface must be free of oil, grease and other contaminants.
CLEAN UP: with High Chloride Polyethylene Thinner X-4

SAFETY: Pay attention to the safety precautions before and after using this product. Users should comply with the provision of the respective country or local government. It’s dangerous or deadly to eating it. To avoid inhalation of thinner steams and spray mists.
Use protective wears correctly; the skin and eyes should avoid contacting it. Use with good ventilation. This product is flammable. All sources of ignition must be eliminated in, or near the working area. DO NOT SMOKE. Fight fire with foam, CO2 or dry chemical powder. On burning will emit toxic fumes.