Introduction to products
PRODUCT NAME Chlorinated Rubber Coat SLX54
BRIEF One Pack antirust paint made from HCPE modified asphalt, modifier,pigments and extenders
FEATURES
-Good adhesion, high hardness
-Excenllent physical properties and chemical corrosion resistance
-Resistance to water, microorganism and plant roots erosion resistance is very strong
-High chlorine content, has good flame retardancy and mildew resistance
-Excenllent water resistance, corrosion resistance and permeability resistance
-Excellent wear resistance、rust-proof and weather ability
-Quick drying, construction is convenient, not restricted by seasonal temperatures
RESISTANCE GUIDE
HEAT RESISTANCE Up to 65℃ dry heat
WEATHERABILITY well
SOLVENTS Resists splash and spillage of aliphatic solvents and mineral oil
ACIDS Resists splash and spillage of most inorganic acid fluid
ALKALIS Resists splash and spillage of most alkalis
SALTS Resists splash and spillage of most alkali salts
WATER Resists splash and spillage of fresh and salt water.
ABRASION Excenllent
USES: Widely used on hull bottom、oil platforms, bridges, marine facilities, mining, underground pipeline, etc
TYPICAL PROPERTIES AND APPLICATION DATA
COLOR Black
DENSITY 1.4g/cm3
SOLIDS BY VOLUME 60%
SOLIDS BY WEIGHT 75%
SPREADING RATE 8.57m2/kg (50um DFT)
DRYING TIME(23℃) Touch 4 Hr Handle 24 Hr
OVERCOAT INTERVAL(23℃) Min 4 Hr
STORAGE at least 12 months (dry, cool and under cover )
PACKAGING 22kg
DIRECTIONS Before using stir or using dynamic mixer mixing two components completely. Rate of cure will vary depending on temperature and other factors such as ventilation, film thickness, humidity, thinner. The temperature of stir will >15℃, otherwise thinner should be added for needed viscosity after stir. Overmuch thinner will lead sag and slow cure rate, thin film, thinner should beadded after mixed. Practical spreading rates may be reduced 5%—25% for wastage of different application conditions.
APPLICATION
STEEL: Steel surface must be prepared by abrasive blast cleaning to ISO Standard Class Sa2.5 or power tool cleaning Class St3. The surface coated by shop primer should be dry, clean and no dirt, take the second descaling where film damaged or corrosion, and achieve Sa2.5 level or St3 level. Clear the zinc salt with high pressure fresh water or sand. Weld and the damage parts processing to Sa2.5 level or St3 level.
Don’t apply at temperatures below-5℃ or above 40℃. Don’t apply at relative humidity above 85% or when the surface is less than 3℃ above the dew point.
Don’t apply if there is fog, rain, snow or strong wind.
BRUSH/ROLLER: Suitable for small areas only. Apply even coats of the mixed material to the prepared surface. Thin if necessary with up to 0-5% with Special Thinner. Additional coats may be required to attain specified thickness.
CONVENTIONAL SPRAY: Thinning is not normally required, however 0-5% of Special Thinner can be added.
AIRLESS SPRAY: Thinning is not normally required, however 0-5% of Special Thinner can be added. Pump ratio is 32:1 or45:1 and fluid tip is 0.43-0.48 mm.
Overcoating: Aged coating should be tested for lifting by a method such as ‘X’cut or crosshatch methods. If it lifts, remove it. The surface must be free of oil, grease and other contaminants.
Previous coat: Epoxy Coatings, HCPE Coatings
CLEAN UP: with Epoxy Thinner X-2
SAFETY: Pay attention to the safety precautions before and after using this product. Users should comply with the provision of the respective country or local government. It’s dangerous or deadly to eating it. To avoid inhalation of thinner steams and spray mists.
Use protective wears correctly; the skin and eyes should avoid contacting it. Use with good ventilation. This product is flammable. All sources of ignition must be eliminated in, or near the working area. DO NOT SMOKE. Fight fire with foam, CO2 or dry chemical powder. On burning will emit toxic fumes.
Notes: The data in the manual is get from standard experiments and may be vary from different conditions in use. Please refer to the latest manual if the data is altered and we would not inform specially.