PRODUCT NAME SLH04 Epoxy Enamel

BRIEF Two Pack Amine Cured Epoxy Topcoat

FEATURES 
-Excellent adhesion on suitable previous coat, good gloss                 
-Good resistance to abrasion and impact                 
-Excellent oil proof and salt spray resistance                 
-Excellent chemical resistance 

RESISTANCE GUIDE
HEAT RESISTANCE  Up to 140℃ dry heat
WEATHERABILITY    Normally not exposed 
SOLVENTS         Resists splash and spillage of most varsol, refined petroleum products and most common alcohols
ACIDS                  Suitable for splash and spillage to mild acids
ALKALIS              Suitable for splash and spillage to strong alkalis
SALTS                  Excellent resistance to neutral and alkali salts
WATER                Excellent resistance to immersion in fresh and salt water
ABRASION         Good when fully cured.

USES:Widely used in ship, oil platform, bridge, marine facilitiess, etc

TYPICAL PROPERTIES AND APPLICATION DATA
COLOR                         Colors
DENSITY                       1.35g/cm3
SOLIDS BY VOLUME              58%
SOLIDS BY WEIGHT               78%
SPREADING RATE                4.3 m2/kg   (100um DFT)
DRYING TIME(23℃)              Touch  4 Hr    Handle  24 Hr    Full cure 7Days
OVERCOAT INTERVAL(23℃)        Min 8 Hr   Max 7 Days 
STORAGE                                at least 12 months (dry, cool and under cover )
PACKAGING                            Part A: 21kg   Part B:3kg
MIXING RATIO (m/m)             Part A : Part B=7:1
CURE TIME(23℃)                 10min
POT LIFE(23℃)                      4 Hr


DIRECTIONS Before using stir or using dynamic mixer mixing two components completely,Just mix a good raw material and mixing of raw materials before can not be together. Rate of cure will vary depending on temperature and other factors such as ventilation, film thickness, humidity, thinner. The temperature of stir will >15℃, otherwise thinner should be added for needed viscosity after stir.
Overmuch thinner will lead sag and slow cure rate, thin film. Practical spreading rates may be reduced 5—25% for wastage of different application conditions.

APPLICATION  STEEL: The surface coated by primer or intermediate paint should be dry and clean, no       oil and other pollutants. When overcoat on a two-component film such as epoxy paint,wharf's pavement quality for old film should be taken if more than the longest accordance with time.
Don’t apply at temperatures below 5℃ or above 40℃. Don’t apply at relative humidity above 85% or when the surface is less than 3℃ above the dew point.
Don’t apply if there is fog, rain, snow or strong wind.
 
BRUSH/ROLLER: Suitable for small areas only. Apply even coats of the mixed material to the prepared surface. Thin if necessary with up to 0-15% with Epoxy Thinner X-2. Additional coats may be required to attain specified thickness. 
CONVENTIONAL SPRAY: Thinning is not normally required, however 0-15% of Epoxy Thinner X-2 can be added.
AIRLESS SPRAY: Thinning is not normally required, however 0-5% of Epoxy Thinner X-2 can be added. Pump ratio is 23:1 or 32:1 and fluid tip is 0.38-0.48 mm.
Overcoating:Aged coating should be tested for lifting by a method such as ‘X’cut or crosshatch methods. If it lifts, remove it. The surface must be free of oil, grease and other contaminants.
Previous coat: Zinc Rich Epoxy Primer, Anticorrosive Epoxy Primer
CLEAN UP: with Epoxy Thinner X-2

SAFETY:Pay attention to the safety precautions before and after using this product. Users should comply with the provision of the respective country or local government. It’s dangerous or deadly to eating it. To avoid inhalation of thinner steams and spray mists.
Use protective wears correctly; the skin and eyes should avoid contacting it. Use with good ventilation. This product is flammable. All sources of ignition must be eliminated in, or near the working area. DO NOT SMOKE. Fight fire with foam, CO2 or dry chemical powder. On burning will emit toxic fumes.

Notes: The data in the manual is get from standard experiments and may be vary from different conditions in use. Please refer to the latest manual if the data is altered and we would not inform specially.